Drizoro - epoxidové pojivo Maxepox Morter
cena na vyžádání
propagační cena
jednotková síť
429,53Kč pro kilogram
minimální komerční
množství produktu
10.00 kilogram
4658,10Kč
pro 10.00 kilogram
4295,26Kč
pro 10.00 kilogram
propagační cena
hrubá jednotka
528,32Kč
pro kilogram
minimální komerční
množství produktu
10.00 kilogram
5729,46Kč
pro 10.00 kilogram
celková cena
propagační sleva
5283,16Kč
pro 10.00 kilogram
Popis produktu
Two-component, chemically hardening binder based on epoxy resins. After mixing with a suitable aggregate, e.g. quartz sand, it is possible to obtain a covering material as well as a mortar with high mechanical and chemical resistance and an aesthetic appearance.
Features
- abrasion resistant
- decorative, available in many colors
- when using a transparent variety, colored aggregates can be used
- the possibility of making a smooth or anti-slip surface of the expedition
- high chemical and mechanical resistance
- easy to keep clean
Application
- floor coverings of concrete slabs in garages, wholesalers, sports centers, etc.
- insulation and surface on communication facilities such as bridges, viaducts, tunnels
- as a multilayer coating with sand sprinkles - on concrete substrates that may be loaded with pedestrians, cyclists and light vehicular traffic,
- as a mortar - on concrete substrates for which loads corresponding to the harsh conditions of road transport are expected - vehicles on steel wheels with an axle load exceeding 6 kN or on pneumatic wheels with an axle load exceeding 50 kN
- as a coating protection for concrete surfaces with a slight slope
Technical data
- color and appearance of component B yellow liquid
- Component ratios in epoxy A: B 2.33: 1 kg
- proportion - binder: aggregate (maximum / minimum) for 1: 5/1: 6 mortar
- solids 100%
- mortar density 2.1 g / cm 3
- service life 10 C / 20 C / 30 C - 120/80/40 min
- hardening time 10 C / 20 C / 30 C 24/18/8 h
- commissioning period 3 days
- compressive strength of the mortar 80.0 MPa
- bending strength of the mortar 25.0 MPa
- modulus of elasticity 12,500 MPa
- linear expansion coefficient 20 x 10 -6 1 / C
- consumption / thickness as epoxy based mortar 2,1; wear as a 0.5 epoxy based coating; recommended thickness for epoxy based mortar 4-5
- 10 kg and 20 kg packaging
Technické údaje - vlastnosti
Přílohy