Popis produktu
910 Renovation Ruler is a factory-prepared mixture of hydraulic binders, mineral fillers with balanced grain size and specialist modifying additives. It is characterized by easy workability and high adhesion to moist and salty substrates. After hardening, water and frost resistant. Does not limit vapor permeability. The product complies with WTA guidelines.
Destiny
910 Renovation Rendering is intended for preparing the base in the KREISEL renovation system, in places exposed to salt and moisture. The product is especially recommended for renovation and conservation of the historic building. Suitable for both plastering and hand application.
Technical data
- bulk density of fresh mortar: approx. 1.80 g / cm3,
- bulk density of hardened mortar: about 1.60 g / cm3,
- compressive strength after 28 days: category CSIV,
- flexural strength after 28 days: 2 MPa,
- adhesion to the ground and symbol of the crack model: 0.5 MPa; FP: A,
- shrinkage after 28 days of hardening: <0.1%,
- water penetration after water absorption test caused by water capillary action:> 5mm,
- water absorption due to capillary uplift: ≤ 0.3kg / m2min0.5,
- water vapor permeability coefficient m: = 15,
- dissolved chromium VI content: ≤ 0.0002%
- storage: up to 9 months from the date of production, in dry places and in undamaged factory packaging,
- the product has the required documents for use.
Technické údaje - vlastnosti
- množství v balení:
- 30 kilogram
- Počet kusů na paletě:
- 42 ks.
- požární klasifikace - reakce na oheň:
- A1
- složení:
- cement portlandzki, wypełniacze mineralne, dodatki modyfikujace
- součinitel tepelné vodivosti λ:
- 0,83 W / mK
- zrnění:
- do 2,0 mm