Maxrite S is a PCC / SPCC filling mortar for repairing a hole in concrete. It is available as a one-component, fine-grained cement-polymer product with microsilica, to be mixed only with water. It has thixotropic properties, thanks to which it allows application up to 5 cm in one layer.

Technical data

• maximum grain size 3 mm
• dry mix density 1.3 0.1 g / cm ³
• mixing with water (by weight) 14 2%
• application setting time (at 20 ° C) initial 3-4 hours; final 7-8 hours
• the density of the hardened mortar 2.0 0.1 g / m ³
• compressive strength after 28 days (EN 12190) from 45 MPa
• ion content in chloride (UNE-EN 1015-17: 2001) up to 0.05%
• adhesion to the substrate (EN1542) from 2.0 MPa
• modulus of elasticity (EN 13142) from 20 GPa
• resistance to carbonation (EN13295) up to 4.0 mm
• capillary absorption (EN 13057) up to 0.5 kg / m ² h ^0.5
• fire resistance class A 1
• adhesion after freeze-thaw cycles (EN 13687-1) from 2.0 MPa
• adhesion after wetting cycles (EN 13687-2) from 2.0 MPa
• adhesion after drying cycles (EN 13687-4) from 2.0 MPa
• layer thickness minimum / maximum 5/50 mm
• consumption 1.7 0.1 kg / m ² / mm

Application

• concrete repair
• concrete replenishment
• leveling concrete
• hydrotechnical and bridge structures
• increasing the thickness of the floors
• protection against carbonation
• resistance to frost and defrosting salts
• water vapor diffusion
• resistance to mechanical stress

Maxrite S can be applied by hand or by dry and wet spraying technology. Non-toxic product.