A water-borne and epoxy primer that inhibits the corrosion process, which forms a highly effective anti-corrosive protective coating, especially on metal surfaces.

Features

• binary
• non-toxic
• creates a protective barrier against water, chlorine ions and gases
• has excellent corrosion inhibition properties
• perfectly adheres to steel and other metal surfaces
• has very good abrasion resistance
• it is not susceptible to moisture absorption
• solvent-free, non-flammable
• as a virtually odorless material, it can be used in poorly ventilated rooms
• demonstrates high durability
• easy to apply and clean

Application

• anti-corrosive protective coating for all metal surfaces such as steel, aluminum or other, intended for use in pipelines, tanks, bridges, metal structures, tunnels
• primer for metal surfaces, intended for use before the application of a polyurethane coating resistant to UV rays, type Maxurethane 2C
• primer for metal surfaces, intended for use before the application of the solvent-free epoxy coating, type Maxepox 800 and Maxepox Flex

Technical data

• 5: 1 component in A and B mixing ratio by weight
• external appearance red liquid
• density 1.34 g / cm ³
• element content in solids 71% by weight
• element by volume in solids 53%
• application and maturation temperature> 10 ° C
• shelf life 10 kg of the product at temperatures of 10 C / 20 C / 30 C - 180/120/60 min
• drying time without sticking of the product at the temperature of 20 C 6-8 h
• total time of maturation and putting into service at 10 C / 20 C / 30 C - 8/5/3 days
• adhesion to metal 5.4 MPa (according to ASTM D-4541)
• consumption ٭ per one layer 0.25 kg / m ²
• thickness of the dry film making up one layer 100 m

* the consumption is indicative and may vary depending on the product used, roughness and condition of the substrate