Two-component injection material based on low-viscosity epoxy resin. It shows high adhesive strength and very good penetrating properties. The product is used for sealing cracks in walls, concrete, wood and natural stone. It can be used to fill cracks with the use of high-pressure, low-pressure and gravity methods.

Features

• good adhesion to moist substrates
• good penetration into the smallest scratches and voids
• low viscosity
• shows high compressive strength, tearing off and cutting
• creates connections resistant to high forces

Technical data

• A: B component ratio (to weight) 3.33: 1
• proportion - resin: aggregate 1: 3
• component A density 1.1 g / cm ³
• density of component B 0.9 g / cm ³
• mixture density at 25 ° C 1.0 g / cm ³
• mixture viscosity at 25 C 280 cPs
• lifetime 100 g at 10 C / 20 C 20/10 min
• exothermic heat 100 g 200 C
• post-reaction contraction (volume / linear) 0.55 / 0.18
• compressive strength: at 20 C 2 h - 410 kp / cm ² ; at 5 C 16 h - 640 kp / cm ^2; at 20 C 7 days - 1100 kp / cm ²
• flexural strength: at 20 C 2 h - 180 kp / cm ² ; at 5 C 16 h 270 kp / cm ² ; at 20 C 7 days - 400 kp / cm ²
• modulus of elasticity at 20 C, 7 days 175,000 kp / cm ²
• transformation temperature 60 ° C
• linear expansion coefficient 75. ^10–6 cm / C
• excellent resistance to chemical attack
• excellent water resistance
• good adhesion to dry concrete (fracture in concrete)
• good adhesion to wet concrete (breakage in concrete)
• 1 kg and 2 kg packaging