Popis produktu
One-component polymer-cement mortar (PCC), containing microsilica, reinforced with synthetic fibers. The product is a repair mortar for filling concrete defects with the Sika Repair-10 F bonding coat. The mortar can be applied by hand or by wet spraying.
Features
- material supplied ready for use, requires mixing only with water
- ease of preparation and application
- resistance to chemical aggression
- class R4 in accordance with PN-EN 1504-3
- good mechanical properties, tightness
Application
- structural and non-structural repairs by manual method concrete in areas exposed to increased environmental aggression, e.g. in general construction, hydrotechnical construction: dams, reservoirs, canals, dams, sewage treatment plants; by industry: pavements, underground workings, shafts
- suitable for repair works (principle 3, methods 3.1 and 3.2 of PN-EN 1504-9) - repairing peeled or damaged concrete in buildings and other reinforced concrete structures (manual application of repair mortar, application of a mortar layer)
- suitable for structural reinforcement (principle 4, method 4.4 of PN-EN 1504-9) - increasing the load-bearing capacity of the concrete structure by adding a mortar layer
- suitable for maintaining or restoring passivity (principle 7, method 7.1 and 7.2 of PN-EN 1504-9) - increasing the thickness of the reinforcement cover and replacing damaged or carbonated concrete
- in the Sika Repair F concrete repair system, local filling the defect in 1-4 cm thick layers on the Sika Repair-10 F bonding layer
Technical data
- chemical base cement, polymer, microsilica, synthetic fibers, selected aggregate, special additives
- appearance / color gray powder
- density ~ 2.06 kg / dm 3 (density of hardened mortar after 28 days)
- maximum grain size D max 4 mm
- content of soluble ions in chloride ≤ 0.05% (according to PN-EN 1015-17)
- compressive strength ≥ 45 MPa, class R4; 28 days: ~ 54 MPa (according to PN-EN 12190)
- modulus of elasticity in compression ~ 27 GPa (according to PN-EN 13412)
- peel strength ~ 2.7 MPa tests with Sika Repair-10 F bonding layer (according to PN-EN 1542)
- thermal compatibility part 1: freeze-thaw ~ 2.4 MPa tests with Sika Repair-10 F bonding layer (according to PN-EN 13687-1)
- reaction to fire class A1 (according to PN-EN 13501-1)
- capillary absorption ≤ 0.5 kg m -2 h -0.5 (according to PN-EN 13057)
- Corrosion test meets (according to PN-EN 13295)
- Sika Repair-13 F mixing ratio: water - 100: 12 by weight - 3 liters of water per 25 kg bag
- theoretical consumption ~ 19.5 kg / m 2 / cm
- layer thickness minimum 1 cm / maximum 4 cm in one laying cycle
- application conditions ambient and substrate temperature min. +5 C / max. +30 C
- suitability for use ~ 60 min (at a temperature of +20 C)
- storage conditions: store in a dry room, in closed and undamaged packages; protect from moisture; best to use within 6 months from the production date
- package 25 kg bag