Ready-to-use organic, mineral adhesive for laying with increased adhesion, without vertical flow and increased deformability. Especially recommended at GreenBuilding.

properties

• does not contain solvent in
• the lowest emission of volatile organic compounds
• environmentally friendly and health user in
• compatible, certified
• high flexibility
• long correction time
• fast and reliable laying
• does not cause stress in the finishing material
• for flooring inside, walls inside and outside
• suitable for ceramic tiles, porcelain stoneware, glass mosaic, large format tiles, shade tiles, stable natural stones on mineral or cementitious surfaces
• suitable for laying on absorbable gypsum and anhydrite substrates without the need for a primer
• very good in wooden and wood-based substrates stable against water

Application

• Keracem Eco Pronto and Rekord Eco Pronto screeds
• screeds made with the use of Rekord Eco and Keracem Eco professional hydraulic binders
• plasterboard walls
• laterogipsy
• cement and cellular concrete blocks
• cement and gypsum plasters
• prefabricated or cast concrete
• cementitious substrates
• anhydrite substrates
• chipboard
• multilayer boards
• porcelain stoneware
• thinning plates
• clinker
• terracotta
• ceramic tiles
• glass mosaic
• ceramic mosaic
• natural stones
• marble
• composites that do not deform or stain due to water absorption
• boards of sound absorbing and insulating material

Technical data

• white paste
• density 1.74 kg / dm ³
• aggregate mineral composition carbonate crystals
• particle size 0-200 m
• storage 12 months in the original packaging
• viscosity 600,000 mPa s, rotor 93 RPM 1 (Brookfield method)
• operating temperature from +5 C to +35 C
• open time ⩾ 30 minutes (according to EN 1346)
• correction time ⩾ 1 h
• flow ⩽ 0.5 mm (according to EN 1308)
• 24 hour pedestrian traffic
• grouting 12 hours a wall / 24 hours a floor
• commissioning 7 days
• capacity 2-4 kg / m ²

* variable depending on the leveling of the substrate and the tile format

Note: Data obtained at a temperature of +23 C, relative humidity 50% depending on the conditions prevailing at the construction site, i.e. temperature, ventilation, absorbability of the substrate and the material being laid.