One-component polyurethane foam used for filling, insulating and insulating assembly gaps at windows, as well as for filling assembly gaps at door frames in accordance with RAL requirements. Very good adhesion to many standard types in building substrates. Especially recommended for making hermetic joints in buildings with a passive standard.

properties

• flexibility tested by an external unit (MPA)> 30%, foam can better compensate for the movements of the element in the building
• approved for use on the German market
• foam with MPA tests tested from 0 C
• for use on surfaces: plaster, wood, metal, concrete, masonry walls, stone, cement and numerous plastics (polyester, polystyrene, hard polyurethane foam, hard PVC)
• only German-language label - a product intended for the German market (no local approvals for use in construction)
• 750 ml container

Technical data

• building material class (according to DIN 4102) B2 - normal flammability, PNDS04-719
• thermal conductivity (according to EN 12667) 0.035 W / (m K)
• tensile strength (according to DIN 53 455) 60 kPa
• stretching before breaking (according to DIN 53 455) 0.5
• shear strength (according to DIN 53 422) 30 kPa
• compressive stress at 10% compression (according to ISO 844) <15 kPa
• foaming (wetted substrate) 0.6
• water connection (0.2 kg water / m of contact surface of the substrate with foam; according to EN 1609) 0.2 kg / m
• cartridge temperature from +5 C to +35 C
• operating temperature (ambient) from +0 C to +35 C
• time after which it does not stick, 30 mm section (depending on temperature and humidity) 8 min
• time after which it can be cut, 30 mm section (the surface should be well moistened): 45 min
• full load capacity after 24 hours
• capacity (foaming in free space) up to 45 l
• raw density after moisturizing (foaming in the gap) 15-25 kg / m
• resistant to permanent temperatures from -40 C to +90 C
• storage in cool, dry rooms, protected from frost in an upright position
• maximum storage time 9 months from the date of production

Note: Performance depends on air temperature and humidity; the substrate should be well moistened.