It is used for gluing mineral wool boards to typical mineral substrates and making a layer reinforced with mineral wool reinforced with a fiberglass mesh. It is used to insulate the external walls of buildings in the technology of a seamless thermal insulation system based on mineral wool facade panels with a disturbed fiber system, parallel to the surface of the panel (laminar) and perpendicular (lamella wool).

Technical data

• Mixing proportions: 5.0-5.5 l of water per 25 kg of glue
• Open work time: approx. 1.5 hours
• Flow: <0.15 mm
• Adhesion
• adhesion to concrete:> 0.6MPa
  • adhesion to mineral wool boards with disturbed fiber arrangement, parallel to the board surface (laminar):> 0.015 MPa
  • adhesion to mineral wool boards with perpendicular fiber arrangement to the board surface (lamella wool):> 0.015 MPa
• Consistency: dry powder
• all technical specifications are given for a relative humidity of 60% and an air temperature of +20 ° C
• Adhesive mortar consumption on a properly prepared surface
• when insulating the building:
• when gluing mineral wool panels with a disturbed fiber system, parallel to the panel surface (laminar) is approx. 4.0 kg / m2
• when gluing mineral wool boards with perpendicular fiber arrangement to the board surface (lamella wool) is approx. 5.0 kg / m2.
• BOLIX WM glue is a dry mix of hydraulic binders, polymer, base of fine-grained mineral fillers and modifying additives.